Electrocatalytic Reduction of Nitrate via Co3O4/Ti Cathode Prepared by Electrodeposition Paired With IrO2-RuO2 Anode
Wang, Chuan1; Cao, Zhifen1; Huang, Hongtao1; Liu, Hong2; Wang, Sha2
2022-06-03
摘要Nitrate pollution is already a global problem, and the electrocatalytic reduction of nitrate is a promising technology for the remediation of wastewater and polluted water bodies. In this work, Co3O4/Ti electrodes were prepared by electrodeposition for the electrocatalytic reduction of nitrate. The morphology, chemical, and crystal structures of Co3O4/Ti and its catalytic activity were investigated. Then, the electrocatalytic nitrate reduction performance of Co3O4/Ti as the cathode was evaluated by monitoring the removal efficiencies of nitrate (NO3--N) and total nitrogen (TN), generation of reduction products, current efficiency (CE), and energy consumption (EC) at different operating conditions. Under the catalysis of Co3O4/Ti, NO3- was reduced to N-2 and NH4+, while no NO2- was produced. After the introduction of chloride ions and IrO2-RuO2/Ti as the anode, NH4+ was selectively oxidized to N-2. The removal efficiencies of NO3--N (at 100 mg/L) and TN after 2 h were 91.12% and 60.25%, respectively (pH 7.0; Cl- concentration, 2000 mg/L; current density, 15 mA/cm(2)). After 4 h of operation, NO3--N and TN were completely removed. However, considering the EC and CE, a 2-h reaction was the most appropriate. The EC and CE were 0.10 kWh/g NO3-N and 40.3%, respectively, and electrocatalytic performance was maintained after 10 consecutive reduction cycles (2 h each). The cathode Co3O4/Ti, which is prepared by electrodeposition, can effectively remove NO3--N, with low EC and high CE.
关键词nitrate removal electrocatalytic Co3O4 Ti reduction IrO2-RuO2
DOI10.3389/fchem.2022.900962
发表期刊FRONTIERS IN CHEMISTRY
ISSN2296-2646
卷号10页码:9
通讯作者Wang, Sha(wangsha@cigit.ac.cn)
收录类别SCI
WOS记录号WOS:000812398500001
语种英语